Composition:
Gold 40%
Palladium 4%
Silver 47%
Copper 8%
Zinc 1%
Balance Ru
Color: Yelow
Applications: OZARK 40 is a yellow colored Type III hard cast gold dental casting alloy. It is designed for use in crowns, inlays, veneer crowns, 3/4 crowns and short span bridgework.
Physical Properites:
| Casting Temperature | 1825F (995C) |
| Melting Range | 1500-1725F (815-940C) |
| Density (gm/cc) | 12.4 |
| Vickers Hardness | Q-125, H-215 |
| Tensile Strength | Q-64,000 psi H-96,000 psi |
| Yield Strength | Q-34,000 psi H-82,000 psi |
| Elastic Modulus | 12,000,000 psi |
| Elongation(%) | Q-32, H-13 |
Recommended Processing:
| Recomended Solders | 615 |
| Recommended Investment | GB |
Spruing:
Single units - Direct method with 8 ga. sprues and adequate resevoirs.
Multiple Units - Indirect Method with runner bars and 8 ga. sprues.
Investment: Use a low-heat gypsum-based investment following the manufacturer's instructions.
Burnout: After adequate set-up time, place ring(s) in oven at room temperature and raise temperature to 1200F (650C) and hold for 1 hour. Add ten minutes for each additional ring.
Melting and Casting: OZARK 40 has a casting temperature of 1825F(995C). An air/gas torch with multiorifice tip and a white flux are recommended. Clean buttons may be remelted with 50% addition of new alloy. Do not overheat the alloy.
Preparing Framework: Casting may be blasted using aluminum oxide. Pickle with a good pickling acid. Shape, finish and polish.
Soldering:Use 615 solder with a paste flux and an air/gas torch.